LORD® 810 Acrylic Adhesive Where To Buy
Product Information
LORD® 810 Low Read-Through (LRT) acrylic adhesive when cured with LORD Accelerator 20GB creates a flexible adhesive system for bonding metals, such as aluminum, galvanized steel and CRS, and engineered plastics, such as PC-ABS. LORD 810 adhesive in combination with LORD Accelerator 20GB delivers fast cure speed and strong bonding with minimal bondline read-through (BLRT). This adhesive system is commonly referred to as either 810/20GB or 810-20GB.
LORD Accelerator 20GB allows precise control of the adhesive bondline thickness due to its content of glass beads. For further detailed information, refer to the LORD Accelerator 20GB data sheet.
Shelf Life
Shelf life is one year when stored below 77°F (25°C) in original, unopened container. Storage temperatures of 40-60°F (4-15°C) are recommended. If stored cold, allow product to return to room temperature before using. Protect from exposure to direct sunlight.
After dispensing product from cartridge, remove the mixing tip immediately and install supplied cartridge plugs to avoid cured adhesive from plugging cartridge.
LORD 810 adhesive is flammable. Do not store or use near heat, sparks or open flame.
Features and Benefits
Aesthetics – bonds thin and flexible substrates with little to no bondline read-through.
Convenient – requires little or no substrate preparation for bonding metals and plastics.
Non-Sag – remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility.
Temperature Resistant – performs at temperatures from -40°F to +300°F (-40°C to +149°C).
Note: Based on test results, LORD 810/20GB adhesive system exhibits post bake/powder coating temperature resistance up to 400°F (204°C) for 90 minutes. Customer specific substrates should always be evaluated for specific application performance.
Environmentally Resistant – resists dilute acids, alkalis, solvents, greases, oils and moisture; provides excellent resistance to indirect UV exposure and weathering.
Uncured Typical Properties*
| Appearance | Black Paste |
|
Viscosity, cP @ 77°F (25°C) Brookfield |
40,000 - 130,000 |
| Density, lb/gal (kg/m3) | 7.8 - 8.1 (935 - 970) |
| Flash Point, °F (°C) | 59 (15) |
| Working Time, min @ 70°F (21°C) | 8 |
| Time to Handling Strength, min @ 70°F (21°C) | 25 |
| Full Cure Time, hour @ 75°F (24°C) | 24 |
| Mixed Appearance | Grey Paste |
Cured Typical Properties*
| Hardness**, Shore D | 40 |
| Tensile Strength at Break**, psi (MPa) | 841 (5.8) |
| Elongation**, % | 190 |
| Glass Transition Temperature (Tg)**, °F (°C) | 109 (43) |
*Data is typical and not to be used for specification purposes.
**Data obtained using LORD 810 adhesive/Accelerator 20GB cured at room temperature.
Auxiliary Products
| LORD<sup>®</sup> Accelerator 20GB |
|
mix-in accelerator; 2:1 mix ratio Features and BenefitsConvenient – provides room temperature cure with all LORD acrylic adhesives. Environmentally Recommended – contains no solvent, non-flammable and virtually odorless. Environmentally Resistant – resists common environmental conditions when used with LORD acrylic adhesives. Bondline Control – allows precise control of adhesive bondline thickness due to content of glass beads, 10 mil (250 μm) diameter. |
Literature
| Download | Type | Name | |
|---|---|---|---|
 |
Technical Data Sheet | LORD 810 Acrylic Adhesive | |
|
|
Product Brochure/Bulletin/Sell Sheet | LORD 810 Acrylic Adhesive | |
|
|
Selector Guide | LORD Structural Adhesives Selector Guide | |
|
|
Powder Coating after Bonding with LORD Acrylic Adhesives | ||
|
|
Safety Data Sheet | LORD 810 |
Related Blog Posts